Grade
| LX004 | LX010 | LX020 | LX100 | LX200 | LX400 | LX900Z | |||
|---|---|---|---|---|---|---|---|---|---|
| Appearance | – | – | Clear and Bright | Clear and Bright | Clear and Bright | Clear and Bright | Clear and Bright | Clear and Bright | Pale white |
| Molecular weight (GPC) (PSt. Std.) |
Mw | – | 2,700 | 4,200 | 5,000 | 8,700 | 11,000 | 12,000 | 16,000 |
| Viscosity (BF) |
25°C 100°C |
mPa·s | 820 30 |
3,000 80 |
6,100 120 |
26,000 480 |
52,000 880 |
140,000 1,600 |
190,000 2,800 |
| Kinematic viscosity | 40°C 100°C |
mm2/s | 400 40 |
1,300 100 |
2,200 150 |
9,800 600 |
18,900 1,100 |
37,500 2,000 |
> 50,000 3,300 |
| Density | 15°C | kg/m3 | 838 | 843 | 846 | 850 | 850 | 851 | 853 |
| Melting point | DSC | °C | Not observed | Not observed | Not observed | Not observed | Not observed | Not observed | –2 |
| Glass transition temperature | DSC | °C | –77 | –71 | –69 | –66 | –65 | –64 | –62 |
| Total acid number | – | mgKOH/g | < 0.01 | < 0.01 | < 0.01 | < 0.01 | < 0.01 | < 0.01 | < 0.01 |
| Flash point | COC | °C | 250 | 280 | 300 | > 300 | > 300 | > 300 | > 300 |
← swipe →
- *Reference standard
- Kinematic viscosity : JIS K 2283:2000 (ISO 2909:1981、ISO 31104:1994)
- Density : JIS K 2249-3:2011 (ISO 3838)
| A-5515 (Acid-modified grade) |
A-5260 (Acid-modified grade) |
|||
|---|---|---|---|---|
| Base LUCANT™ | — | — | LX020 | LX100 |
| Appearance | — | — | Clear Yellow | Clear Pale Yellow |
| Molecular weight (GPC) (PSt. Std.) |
Mw | — | 7,200 | 10,000 |
| Viscosity (BF) |
25°C 150°C |
mPa·s | 53,000 70 |
61,000 160 |
| Density | 15°C | kg/m3 | 878 | 860 |
| Melting point | DSC | °C | Not observed | Not observed |
| Glass transition temperature | DSC | °C | –65 | –64 |
| Total acid number | — | mgKOH/g | 60 | 25 |
| Flash point | COC | °C | 280 | 290 |
← swipe →
- *Reference standard
- Density : JIS K 2249-3:2011 (ISO 3838)
*The data shown above are typical and not guaranteed.